​321H stainless steel has good corrosion resistance, especially in oxidizing medium has good corrosion resistance. Because of its good heat resistance and oxidation resistance, it is more used as a heat resistant steel. Comparing with 321 Stainless steel, [SCALE STEEL]321H has higher Carbon content and similar properties with 321 Stainless. 
 
A. 321H Corresponding Brand:  
1, GB GB-T standard: digital brand number: S32169, new brand number: 07Cr19Ni11Ti, old brand number: 1Cr18Ni11Ti;  
2, American standard: ASTM standard: [SCALE STEEL]S32109, UNS standard: 321H;  
3, JIS standard: SUS321HTB;  
4, DIN standard: 1.4940,1.4541;  
5, European standard EN standard: "X8CrNiTI18-10, X7CrNiTI18-10;  
6, NF standard: /;  
7, British BS standard: 321S20.  
 
B. 321H Stainless Steel Chemical Composition:  
⑴ carbon C: 0.04~0.10⑵ silicon Si: ≤0.75, [SCALE STEEL]⑶ manganese Mn: ≤2.00, ⑷ phosphorus P: ≤0.030, ⑸ sulfur S: ≤0.030,[SCALE STEEL] ⑹ chromium Cr: 17.00 ~ 20.00, ⑺ nickel Ni: 9.00 ~ 13.00, other elements: Ti≥4C~0.60.  
 
C. 321H Stainless Steel Physical Properties:  
Density Density (20℃) /kg/dm3:"8.03,, magnetism: none.  
 
D. 321H Stainless Steel Mechanical Properties:  
(1) Delivery status: solid solution treatment of bar, solid solution pickling of plate;  
⑵ Tensile strength (RM/MPa) 520;  
⑶ Elongation strength[SCALE STEEL] (Rp0.2/MPa) : 205;  
⑷ Elongation A/% : 40;  
⑸ Area shrinkage (Z/%) : 50.  
 
E. 321H Stainless Steel Heat Treatment:  
1. Hardness HBW≤ : solution 187, hardness HRB≤ : 90;  
2. Heating temperature: 920~1150;  
3. Heating method: fast cooling.  
 
321H Stainless Steel’s Application:
321H Stainless Steel is [SCALE STEEL]widely used for boiler superheater, heat exchanger, condenser, catalytic tube, cracking tube device and other steel tubes and fittings.  

GS-25CrNiMo4 alloy is one kind of special Cr-Ni-Mo Alloy which is suitable used under the environment with temperature up to 300℃[SCALE STEEL].
 
Chemical Composition for GS-25CrNiMo4 Alloy:
 
C(％):0.22-0.29
Si(％):0.30-0.60
Mn(％):0.60-1.00
P(％):Max 0.025
S(％):Max 0.025
Cr(％):0.80-1.20
Ni(％):0.80-1.20 [SCALE STEEL]
Mo(％):0.20-0.30
 
Mechanical Property for GS-25CrNiMo4 Alloy:
 
Proof Strength Rp0.2(MPa):350-400
Tensile Strength Rm(MPa):650-850
Impact Energy KV(J):24
Elongation at Fracture A(%):21
Reduction in Cross [SCALE STEEL]section on Fracture Z(%):43
As-Heat-Treated Conditions:Solution and Aging,Annealing,Ausaging,Q+T,etc
Brinell Hardness(HBW):442
 
For Moe Infos about GS-25CrNiMo4, pls feel free to contact us.
 
 
 

​I. Introduction of 12Ni14 Nickel Alloy Plate  
12Ni14 is a boiler pressure vessel steel plate, using the European standard brand, 12Ni14 is a nickel alloy steel plate used in pressure equipment, [SCALE STEEL]the common brand of European standard container plate are: HII/P265GH P275NH P275NL P355GH P355NH P355NH P355NL1 P460NH 16Mo3, etc  

2. The Implementation Standard of 12Ni14 Steel Plate: EN10028-4(Hot Rolled Type), EN10222-2( Forged Type)  

3. Delivery Status of 12Ni14 Steel Plate:  
The steel plate is usually delivered by normalizing, [SCALE STEEL]normalizing and tempering, quenching and tempering 

4. Chemical Composition of 12Ni14(%):
C: ≤0.15
Si: ≤0.35
Mn: 0.30-0.80[SCALE STEEL]
P: ≤0.020
S: ≤0.005
Ni: 3.25-3.75
V: ≤0.05

5.Mechanical Property of 12Ni14 Alloy:
[GRADE] [DELIVERY STATUS] [THICKNESS
/MM] [YIELD STRENGTH
/MPa] [TENSILE STRENGTH/MPa] [ELONGATION/% MIN.]
[EN10028-4 12Ni14
/ EN10222-3 12Ni14] [N/N+T/Q+T] [≤30] [≥355] [490-640] [22]
[30-50] [≥345]
[50-80] [≥335]


6. Main Applications of 12Ni14 Alloy:
12Ni14 is one kind of nickel [SCALE STEEL]alloy materials for pressure equipment especially under low temperature, mainly used in building of pressure equipment, boiler, pressure vessel, LNG tanks, etc.