Product Introduction
UNS N06030 is a nickel-based alloy with a high chromium content of about 37% nickel, which provides better corrosion resistance than most other nickel-based and iron-based alloys to commercial phosphoric acid [SCALE STEEL]and the mixed environments of many highly oxidizing acid media such as nitric/hydrochloric acid, nitric/hydrofluoric acid and sulfuric acid. N06030 can prevent the formation of grain boundary precipitation in the welding heat affected zone, so its soldered products are suitable for a variety of chemical treatment engineering applications. Chemical Composition (%): Ni:Rest; Cr: 28-31.5; C: 0.03 Max; Fe:13-17; Mo:4-6; W: 1.5 4; Cu: 1-2.4;[SCALE STEEL] Co:5max; Si: 0.2-0.8; Mn: 0.3-1.5; P: 0.04 Max; S: 0.02 Max; Nb: 0.3-1.5; Physical Property Density: 8.23 g/cm after; Melting Point:1335-1380℃; Electrical Resistivity:1.28; Thermal Conductivity:14;[SCALE STEEL] Specific Heat Capacity:398; Mechanical Property Heat Treatment:Solution&Annealed; Tensile Strength:586MPa min; Yield Strength: 241MPa min;[SCALE STEEL] Elasticity Modulus:212 min; Elongation: 30% min; Product Standard UNS N06030 Bar-ASME SB581; UNS N06030 Plate-ASME SB582; UNS N06030 Seamless Pipe-ASME SB622; UNS N06030 [SCALE STEEL]Welded Pipe-ASTM B619,ASTM B626; UNS N06030 Forged Products-ASTM B462,etc. Product Characteristics A. Excellent corrosion resistance in alkaline media; B. Good corrosion resistance against cavitation; C. Has good corrosion resistance to diluted [SCALE STEEL]inorganic acids (such as sulfuric acid, hydrochloric acid); Application Field A.Chemical process equipment; B.High temperature heat exchanger; C.Catalyst carrier;[SCALE STEEL] D.Petrochemical storage tanks; E.Components of nuclear equipment; Product Introduction
UNS N06002 is a nickel-chromium alloy with the addition of drill and tungsten. The alloy has excellent oxidation resistance[SCALE STEEL] at high temperatures up to 1200℃ and can also be used in neutral and reductive atmospheres. At the same time, the alloy can resist carbonization and nitriding atmosphere. Chemical Composition (%): Ni:Rest; W: 0.2-1.0; Fe:17-22; Mn: 1.0 Max; C: 0.05-0.15; Si: 1.0 Max;[SCALE STEEL] S: 0.03 Max; Cr: 20.5-23; Mo:8-10; P: 0.04 Max; Co: 0.5-2.5; Physical Property Density: 8.28 g/cm after; Melting Point:1260-1355℃; Mechanical Property[SCALE STEEL] Tensile Strength:690MPa min; Yield Strength:276MPa min; Elongation(%):35min; Product Standard N06002 Bar-ASTM B572; N06002 Plate-ASTM B435; N06002 Seamless Pipe-ASTM B622; N06002 Welded Pipe:ASTM B619;[SCALE STEEL] N06002 Pipe Fitting-ASTM B626; N06002 Forged Product-ASTM B575,etc. Product Characteristics A. Good cold and hot processing performance; B. With satisfactory welding performance, it can be welded by argon arc welding, seam welding, spot welding and other [SCALE STEEL]methods; C. The adhesion of surface oxides and welding slag around the weld is stronger than that of stainless steel; Application Field 1.Industrial and aerospace turbines; B.Spiral tubes in petrochemical furnaces; C.Industrial furnace components (support rolls, grids, ribbons and radiation tubes); D.High temperature gas cooled nuclear reactors; E.Industrial and aviation[SCALE STEEL] steam turbines F.Spiral tubes in petrochemical furnaces G.Industrial furnace components (support rolls, grids, ribbons and radiation tubes) H.High temperature gas cooling nuclear reactors |
nEWSFROM SCALE STEEL ARCHIVES
October 2024
Categories |