06Cr13 (0Cr13),410S,SUS410S,1.4000 Martensitic (Ferrite) Stainless Steel- SCALE STEEL.

3/25/2021

 
06Cr13, the American standard 410S, is the lowest carbon content in the Cr13 martensitic stainless steel.Due to the microstructure of[SCALE STEEL] the matrix under annealing condition, it is also classified as ferritic stainless steel in a few standards.

Standard Control
CHINA GB/T 20878-2007 S41008 06Cr13
(0Cr13)
GB/T 24511-2009 S11306
AMERICA ASTM A240-15a S41008,410S
JAPAN JIS G 4304:2005 SUS410S
GERMANY DIN EN 10088-2:1995[SCALE STEEL] X6Cr13,1.4000

Component Specification
GRADE 06Cr13* 410S SUS410S 1.4000
C ≤0.08 ≤0.08 ≤0.08 ≤0.08
Si ≤1.00 ≤1.00 ≤1.00 ≤1.00
Mn ≤1.00 ≤1.00[SCALE STEEL] ≤1.00 ≤1.00
P ≤0.040 ≤0.040 ≤0.040 ≤0.040
S ≤0.030 ≤0.030 ≤0.030 ≤0.015
Cr 11.5~13.5 11.5~13.5 11.5~13.5 12.0~14.0
Ni (≤0.60) ≤0.60 (≤0.60) --
*:S41008 is listed in the table, while S11306 is slightly different in composition.

Mechanical Property
Density(g/cm3)20℃[SCALE STEEL] 7.75
Specific heat [kJ/(kg·K)]  0~100℃ 0.46
Heat conductivity [W/(m·K)] 100℃ 25.0
coefficient of linear expansion(10-6/K) 0~100℃ 10.6
0~500℃ 12.0
specific resistance(Ω·mm2/m)20℃ 0.60
longitudinal modulus of elasticity(kN/mm2)20℃ 220
magnetism Y

Mechanical Property

Dimensions of sample hairs(mm) ≤75
heat treating regime anneal[SCALE STEEL] 800 ~ 900 ℃ slow cooling
Or about 750℃ fast cooling

quench 950 ~ 1000 ℃ cold oil
temper 700~750℃cold oil
Mechanical properties 
(quenching + tempering)
Specified non-proportionality
Extension strength MPa ≥345
strength of extension MPa ≥490
Percentage elongation after fracture % ≥24
Percentagereduction of area; reduction of area ≥60
The hardness of delivery HBW anneal ≤183

Material Characteristics:
(1) The corrosion resistance and corrosion resistance are similar to 1Cr13 (410) and better, in low concentration of mild organic and [SCALE STEEL]inorganic acid, alkali and some chemical conditions have corrosion resistance.
(2) Good oxidation resistance, sustainable use in 705℃ environment.
(3) good plastic toughness, easy to be formed by rotation, bending and rolling.
(4) It can be welded by common fusion and resistance technology.

Applications:
The main product form [SCALE STEEL]is plate, used for structural parts such as automobile muffler and exhaust system components, but also widely used in containers, heat exchangers, underground pipes, etc.

Comments are closed.

    nEWS

    FROM SCALE STEEL
    [email protected]

    ARCHIVES

    April 2025
    December 2024
    October 2024
    September 2024
    July 2024
    June 2024
    May 2024
    April 2024
    March 2024
    February 2024
    January 2024
    December 2023
    November 2023
    September 2023
    August 2023
    July 2023
    June 2023
    April 2023
    March 2023
    February 2023
    January 2023
    December 2022
    November 2022
    September 2022
    July 2022
    May 2022
    March 2022
    February 2022
    January 2022
    December 2021
    November 2021
    October 2021
    September 2021
    August 2021
    July 2021
    June 2021
    April 2021
    March 2021
    February 2021
    January 2021
    December 2020
    November 2020

    Categories

    All

    RSS Feed

HENAN SCALE IMPORT& EXPORT CO.,LTD
[email protected] T:+8637186107816 F:+8637163797816

Copyright © 2018

  • Home
  • About
  • Contact
  • SCALE STEEL NEWS