316Ti Stainless Steel- SCALE STEEL.
316Ti stainless steel plate is named 0Cr18Ni12Mo2Ti in international standard, and Chinese brand name is 1Cr18Ni12Mo2Ti stainless [SCALE STEEL]steel plate, 316Ti stainless steel plate is added Ti element in SUS316 to improve the resistance to intergranular corrosion. 316Ti stainless steel is used for equipment to resist sulfuric acid, phosphoric acid, acetic acid and acetic acid.
Physical Properties of 316Ti Stainless Steel:
C: 0.08 or less
Si 1.00 or less
Mn 2.00 or less
P 0.035 or less
S 0.030 or less
Ni 10.00 ~ 14.00 [SCALE STEEL]
Cr 16.00 ~ 19.00
Mo 1.80 ~ 2.50
Ti acuity 0.2 ~ 0.70
GB/T1220-1992 has this provision, usually also called Mo2Ti or 316Ti
YS (Mpa) ≥205
TS (Mpa) ≥520
EL (%) ≥40
Hv around 200 °
Thickness: cold-tied 2B plate (0.09 -- 6.0mm);
Hot rolled industrial plate No.1(3-50mm) [SCALE STEEL]medium thick plate, chemical plate, high temperature plate;
Width: 5mm-- 850mm steel belt;
1000, 1219, 1250, 1500, 1800, 2000mm coil plate, plate
Surface: 2B smooth surface, No.1 industrial surface, BA (6K) mirror, 8K mirror, 9K mirror, drawing surface, frosted surface.
Origin: Domestic, imported (Sweden,[SCALE STEEL] Japan, Finland, South Korea, South Africa, Taiwan)
Key Properties of 316Ti Stainless:
These attributes refer to products in similar, but not identical, attributes that are specified in other products, such as plates and forgings in their respective specifications. The lower minimum pre - and post-heat[SCALE STEEL] temperatures reduce the incidence of weld cracking and simplify welding. Low hardness decreases the heat affected zone to minimize deterioration in mold performance.