JIS G4053 SCM435 Alloy Steel- SCALE STEEL.

8/10/2021

 
SCM435 has high static strength, impact toughness and high fatigue limit, higher hardenability than 40Cr, high creep strength and durable strength at high temperature, long-term working temperature can reach 500℃;  [SCALE STEEL]Cold deformation plastic medium, poor weldability.  Important structural parts used for working under high load, such as transmission parts of vehicles and engines;  Turbine generator rotor, spindle, heavy load transmission shaft, large section parts.  
 
 
Species  
Alloy Structural Steel: SCM435  
Implementation Standard: JIS G4053-2008  
 
Chemical Composition of SCM435  
C: 0.33 ~ 0.38 Si: 0.15 ~ 0.35  
Manganese Mn: 0.60 ~ 0.90  
Sulfur S: Allowable [SCALE STEEL]residual content ≤0.030  
Phosphorus P: Allowable residual content ≤0.030  
Cr: 0.90 ~ 1.20  
Nickel Ni: Permissible residual content ≤0.25  
Cu Cu: Permissible residual content ≤0.30  
Mo: 0.15 ~ 0.30  
 
SCM435 Standard  
SCM435 standard :SCM435 [SCALE STEEL]is the Japanese standard (JIS G4053-2008) steel, the domestic corresponding steel 35CrMo  
 
SCM435 Hardness  
The hardness of SCM435 is HRC36 ~ 43, HB269 ~ 341  
 
Mechanical Properties of SCM435 
Tensile Strength (MPa) : ≥985(100)  
Yield Strength σs (MPa) : ≥835(85)  
Elongation δ5 (%) : ≥12  
Section Shrinkage rate ψ (%) : ≥45  
Impact Energy Akv (J) : ≥63  
Impact Toughness αkv (J/cm²)  A: 78 (8) or  
Hardness: 229 hb or less  
Sample Size: [SCALE STEEL]sample blank size is 25mm  
 
Heat Treatment Specification  
Heat Treatment Specification: quenching 850℃, oil cooling;  Tempering 550℃, water cooling, oil cooling.  
Delivery Status: heat treatment (normalizing, annealing or high temperature tempering) or no heat treatment, delivery [SCALE STEEL]status should be indicated in the contract.  Annealing no.1 "annealing at 760±10℃, furnace cooling to 400℃ air cooling.  
HB220-230  
860±10℃ normalize, air cooling out of the oven.  
Quenching water or oil (depending on the complexity of product type), 680-700 degrees tempering.  HB<217  
Quenching oil at 840±10℃ and then tempering at 470 ℃.  HRC41-45  
Quenching oil at 840±10℃ and then tempering at 480 ℃.  HRC35-45  
Tempering +tempering No.8 quenching oil at 850℃ and tempering at 510 ℃.  HRC38-42  
Tempering +tempering No.9 quenching oil at 850℃ and then tempering at 500 ℃.  HRC40-43  
Tempering +tempering [SCALE STEEL]No.10 quenching oil at 850℃ and tempering at 510℃.  HRC36-42  
Quenching oil at 850℃ and then tempering at 560℃.  HRC32-36  
Oil quenching at 860℃ and tempering at 390 ℃.  HRC48-52  
 

Comments are closed.

    nEWS

    FROM SCALE STEEL
    [email protected]

    ARCHIVES

    April 2025
    December 2024
    October 2024
    September 2024
    July 2024
    June 2024
    May 2024
    April 2024
    March 2024
    February 2024
    January 2024
    December 2023
    November 2023
    September 2023
    August 2023
    July 2023
    June 2023
    April 2023
    March 2023
    February 2023
    January 2023
    December 2022
    November 2022
    September 2022
    July 2022
    May 2022
    March 2022
    February 2022
    January 2022
    December 2021
    November 2021
    October 2021
    September 2021
    August 2021
    July 2021
    June 2021
    April 2021
    March 2021
    February 2021
    January 2021
    December 2020
    November 2020

    Categories

    All

    RSS Feed

HENAN SCALE IMPORT& EXPORT CO.,LTD
[email protected] T:+8637186107816 F:+8637163797816

Copyright © 2018

  • Home
  • About
  • Contact
  • SCALE STEEL NEWS